| 摘要 |
Air-hardenable steels of duplex bainite/martensite microstructure consisting essentially of 0.10 to 0.7% C, 0.1 to 2% Si, 2.1 to 3.5% Mn, 0.0005 to 0.005% B, up to 3.5% Cr and preferably containing Cr in amount of at least 0.1%, balance Fe except for incidental impurities. Optional elements are up to 1.5% W, 1.0% Mo, 0.15% V, 0.2% S, 0.1% Ca, 0.1% Pb, 0.1% Ti and 0.2% total rare earths. At least 1.0% Cr is especially preferred and if below such amount, total Mn and Si is at least 3% and in such case, if C is under 0.47%, at least 0.6% Si is present. The steels are hardenable to Rc 20 to Rc 58 and have a hardenable diameter in the range between 35 mm and 80 to 100 mm by air-cooling only, together with good strength, toughness and fatigue- and wear-resistance.
|