| 摘要 |
A process for preparing a tetragonal barium titanate film with a thickness of from about 0.1 to about 1.5 millimeters is disclosed. In the first step of this process, a mixture of a barium compound, a titanium compound, and a boron oxide glass former is provided in a specified ratio. The reaction mixture is melted at a temperature of 1300-1400 degrees centigrade and then rapidly quenched in form glass. The glass is then place upon a polycrystalline isostructural substrate, and the glass/substrate assembly is then remelted and, thereafter, subjected to a temperature of from 950 to 1,050 degrees centigrade for from about 25 to about 60 minutes.
|