VERFAHREN ZUR HERSTELLUNG EINER KORROSIONSBESTAENDIGEN VAKUUMHARTLOETSCHICHT.

摘要

A novel process for producing aluminum composite sheet products for roll forming and vacuum brazing is disclosed, which provides an unexpected improvement in the corrosion resistance of the brazed product. According to the process, a composite sheet is annealed to a strain-free state after having been rolled to a thickness which is a critical amount greater than the thickness ultimately sought. Following the annealing step, the sheet is cold worked to the desired thickness, the degree of reduction in this final step being within a critical range which provides the improvement in corrosion resistance to the final product after vacuum brazing.