Method for producing cadmium free green emitting CRT phosphor

摘要

A cadmium-free cathodoluminescent phosphor composition consists essentially of zinc sulfide activated with from about 0.019% by weight to about 0.024% by weight of copper and from about 0.01% by weight of about 0.02% by weight of aluminum wherein the emission of the phosphor upon stimulation by cathode rays has CIE values of x of from 0.287 to 0.291 and y from 0.616 to 0.620. The process involves solid state heating of the various raw materials wherein a first relatively pure zinc sulfide and a second zinc sulfide containing chloride ions are mixed with the appropriate levels of and alkali metal chloride and sources of copper and aluminum activators and then heated in a nitrogen-carbon disulfide atmosphere for about 3 hours at 1775 DEG C. to about 1825 DEG C.