| 摘要 |
Superconducting ceramic articles such as those represented by the general formula YBa2Cu3O7-x where 0<x<0.6 and a process for making them is described. Starting materials for such articles include sources of yttria, cupric oxide and barium monoxide. The mixed ceramic material, are heated to a temperature greater than 30 percent of the materials melting temperature, but less than said melting temperature, and thereafter at least 80,000 sufficient isostatic pressure to consolidate the ceramic material into a body having a density of at least 85 percent of the theoretical density of the materials. The ceramic article may be further modified by annealing and cooling in the presence of oxygen. |