| 摘要 |
<p>A method of heat treating a body of corrosion resistant steel which is, preferably, in coil form, having an austenitic to ferrite and carbide transformation temperature lying between 650 DEG C and 850 DEG C and a composition which results in a steel preferably having mechanical properties typically as follows: Proof stress 350MPa, ultimate tensile stress 520MPa, elongation 25% and Brinell hardness 165 and from which Martensite microstructures are generally absent at cooling rates lower than 5 DEG C/min and where the method comprises: hot working the steel body at above the transformation temperature; cooling the hot worked steel body to below the transformation temperature at a cooling rate of between 10 DEG C/min and 1 DEG C/min determined to ensure generally the absence of Martensite microstructures throughout the body.</p> |