发明名称 |
MANUFACTURE OF OXIDE SUPERCONDUCTOR WIRE |
摘要 |
PURPOSE:To prevent defects such as cracks from being produced by mixing two oxides of specific compositional ratios together with the mol mixing ratio of 1:X (X>=1) followed by a direct heat treatment in an oxygen atmosphere. CONSTITUTION:A first material oxide of the compositional ratio of A2B1Cu1O5 and a second material oxide of the compositional ratio of B3Cu5Oy are mixed together with the mol mixing ratio of 1:X (X>=1). After press-forming the mixed oxide 5 around a metallic core body 4, the product is packed into a metallic pipe and processed by wire drawing process to make a wire material 1. The wire material is then removed of a metallic layer 3 to expose the wire body 2 and heated in the atmosphere at temperature of 800-950 deg.C for a period of 6-50 hours. As a result, the first material powder and the second material powder diffusion-react at their contacting portion to become a superconductor layer 6. The product is gradually cooled to obtain a superconductor wire 7. (The element A is in the group IIIa and the element B is in the group IIa.) This makes it possible to prevent defects such as cracks from being produced and to manufacture a superconductor wire having an excellent superconductive characteristic. |
申请公布号 |
JPH01241709(A) |
申请公布日期 |
1989.09.26 |
申请号 |
JP19880070144 |
申请日期 |
1988.03.24 |
申请人 |
FUJIKURA LTD |
发明人 |
KUME ATSUSHI;IKENO YOSHIMITSU;GOTO KENJI |
分类号 |
C04B35/00;B28B1/00;C01G1/00;C04B35/45;H01B12/04;H01B13/00 |
主分类号 |
C04B35/00 |
代理机构 |
|
代理人 |
|
主权项 |
|
地址 |
|