| 摘要 |
<p>PURPOSE:To simply obtain an inexpensive fibrous laminate rich in decorative properties and excellent in moldability and shape retentivity, by incorporating a resin having a specific glass transition point or higher contained as an emulsion in a fiber mat layer in a specific amount as a resin solid. CONSTITUTION:A fibrous laminate is formed by laminating a skin material E to a laminated mat D which is constituted of upper and lower fabric layers A, B each formed from a thermoplastic fiber binder nonwoven fabric having a m.p. of 60-200 deg.C and a fiber mat layer C based on a synthetic or natural fiber having a m.p. more than 40 deg.C higher than that of the thermoplastic fiber binder nonwoven fabric and has such a structure that the fibers of the fiber binder nonwoven fabrics of the upper and lower fabric layers A, B are bonded to the fibers of the fiber mat layer C in an entangled state. A resin having a glass transition point of 50 deg.C or more is contained in the fiber mat layer C in an amount of 10-100 pts.wt. per 100 pts.wt. of the fiber as an emulsion resin solid. When the emulsion resin solid is smaller than the above mentioned range, rigidity can not be improved and the improvement of shape retentivity can not be expected. When said solid is too much, the laminate becomes too hard.</p> |