In a conventional process for producing a semi-processed non-oriented electrical steel sheet, the silicon or aluminum content of a hot-rolled steel strip is high, especially in the case of producing a high-grade electrical sheet which has a low watt loss. However, a high silicon or aluminum content disadvantageously results in a decrease in the magnetic flux density. A decrease in the watt loss and an increase in the magnetic flux density in semi-processed non-oriented electrical steel sheets as compared with conventional high-grade semi-processed non-oriented electrical steel sheets can be achieved by making the silicon content, which increases resistivity, low, i.e. from 0.1 to 1.0%, and the manganese content, which is effective for improving the texture, high i.e. from 0.75 to 1.5% and by subjecting the starting material, having a low silicon content, and a high manganese content to an appropriate production process for controlling texture.
|