Polypropylene resin prefoamed particles

摘要

Prefoamed particles consisting essentially of an ethylene/propylene random copolymer, wherein said prefoamed particles are obtained by foaming particles of an ethylene/propylene random copolymer containing 1 to 4% by weight of random-copolymerized ethylene at a temperature in the range of from Tm - 15 DEG C. to Tm - 5 DEG C. (in which Tm is a temperature at which to terminate melting of the copolymer) and within the range of 141 DEG to 151 DEG C., and wherein said prefoamed particles have a crystal structure characterized in that in a DSC curve obtained by heating 1 to 3 mg of the copolymer prefoamed particles to 220 DEG C. at a heating rate of 10 DEG C./min. with a differential scanning calorimeter, there appear a peak (characteristic peak) characteristic of the copolymer and another peak (high temperature peak) at a higher temperature than a temperature at which the characteristic peak appears.