| 摘要 |
A glass fiber reinforced poly(ethylene terephthalate) resin, comprising: (i) a poly(ethylene terephthalate) resin; (ii) 10to 60 weight % of reinforced glass fibers; and (iii) 0.1 to 10 weight % of a nucleating agent comprising: (a) a Group I, II, or IV metal cation salt of an ethylene/methacrylic acid copolymer resin having a melt flow index of from about 0.5 g/10 minutes to about 150 g/10 minutes measured at 190 DEG C. under a 10,128-gram load, and (b) a Group I, II, or IV metal cation salt of an ethylene/acrylic acid copolymer resin having a melt flow index of from about 0.5 g/10 minutes to about 150 g/10 minutes measured at 190 DEG C. under a 2,160-gram load.
|