| 摘要 |
PURPOSE:To reduce roughness and ruggedness after brazing and to inhibit tarnish and corrosion by residual cleaning soln., by specifying the compsn. of a Pd alloy filler metal for brazing. CONSTITUTION:This Pd alloy filler metal for brazing has a compsn. consisting of, by weight, 15-35% Cu, 5-25% Pd, 0.001-1.5% P, 0.001-1.0% Si and the balance Ag. The reason that P and Si are contained in the Pd alloy filler metal is that P and Si reduce the surface tension of the filler metal during brazing, suppress the surface roughening of the filler metal and inhibit the occurrence of ruggedness. The P and Si contents are limited because <0.001% P or Si can not inhibit the surface roughening of the filler metal and the occurrence of ruggedness and >1.5% P or >1.0% Si causes the flow of the filler metal to stain the base metal and imparts unfavorable influence on brazing strength.
|