摘要 |
Porous, hollow, silica-rich fibers with good alkaline tolerance are produced from hollow glass fibers of an alkali metal borosilicate glass having one or more oxides of a metal of Group IV of the Periodic Table in an amount of about 1 to about 20 weight percent of the glass composition. The hollow porous silica-rich fibers are produced by acid leaching where the hollow glass fibers have greater than 25 weight percent extractable components, less than 25 weight percent extractable components but a wall thickness of less than 15 microns, or less than 25 weight percent extractable components and a fiber diameter of less than 25 microns. In addition, heat treating can be used for hollow glass fibers having greater than 25 weight percent extractable components to enlarge the pores.
|