发明名称 |
Process for producing nickel steels with high crack-arresting capability |
摘要 |
A process for producing a Ni-steel with high crack-arresting capability is disclosed. The process comprises the steps of: heating a steel material containing 2.0-10% of Ni to a temperature between 900 and 1,000 DEG C.; hot rolling the steel material to provide a cummulative reduction of 40-70% at 850 DEG C. or below, and finishing the rolling operation at 700 DEG -800 DEG C.; immediately after completion of the rolling step, quenching the steel material to a temperature not higher than 300 DEG C.; and subsequently tempering the quenched slab at a temperture not higher than the Ac1 point.
|
申请公布号 |
US4776900(A) |
申请公布日期 |
1988.10.11 |
申请号 |
US19870106916 |
申请日期 |
1987.10.05 |
申请人 |
NIPPON STEEL CORPORATION |
发明人 |
YANO, SEINOSUKE;SAITO, NAOKI |
分类号 |
C21D8/02;C21D8/00;C22C38/08;(IPC1-7):C21D8/00 |
主分类号 |
C21D8/02 |
代理机构 |
|
代理人 |
|