Zirconium alloy fuel cladding resistant to PCI crack propagation

摘要

This invention relates to a tubular water reactor fuel cladding having an outer cylindrical layer composed of a conventional zirconium base alloy. Bonded to the outer layer is a second, inner layer composed of an alloy consisting essentially of: about 0.1 to 0.3 wt. % tin; about 0.05 to 0.2 wt. % iron; about 0.05 to 0.4 wt. % niobium; about 0.03 to 0.1 wt. % of either chromium or nickel, alone or in combination with each other; while keeping the sum of the iron chromium and nickel contents below 0.25 wt. %; 300 to 1200 ppm oxygen; and the balance essentially zirconium. The inner layer is characterized by excellent resistance to PCI crack propagation, excellent aqueous corrosion resistance and a fully recrystallized microstructure.