| 摘要 |
A rubber composition for an inner liner of a vehicular tire, having high crack formation preventing characteristics even during vehicle cruising at low temperatures. The rubber composition comprises a rubber component and a softener. The rubber component includes halogenated butyl rubber ranging from 60 to 100 parts by weight and diene rubber not more than 40 parts by weight. The softener ranges from 3 to 15 parts by weight relative to 100 parts by weight of the rubber component and includes a paraffin component constituting not less than 60 weight % and an aromatics component constituting not more than 5 weight %. Additionally, the rubber component after vulcanization has a storage elastic modulus at 10 DEG C., not higher than 1.4x108 dyn/cm2, and a storage elastic modulus at -45 DEG C., not higher than 8.0x109 dyn/cm2.
|