METHOD OF MANUFACTURE OF THERMOPLASTIC ELASTOMER COMPOSITIONS

摘要

(A) polypropylene (10-90 weight part), (B) halogenated butyl rubber (90-10 weight part, (A) + (B) = 100 weight part), (C) olefinic rubber (10-120 weight part) and (D) mineral oil softening agent (5-120 weight part) are heated in the presence of (E) metal oxide and/or metal chloride. To 100 weight part of the resulting composition are added, (F) polyolefin (100-600 weight part) and (G) vulcanizable olefinic rubber (50-500 weight part) and the components are mixed and heated in the presence of (H) organic peroxide. The resulting thermoplastic elastomer composition has good paintability, moldability, compatibility, low temperature impact strength, and especially high stiffness at elevated temperature.