| 摘要 |
PURPOSE:To provide the titled resin compsn. which has excellent resistance to low-temperature impact, heat and gasoline and gives moldings which can be subjected to on-line coating, consisting of an arom. polycarbonate a thermoplastic polyester, a thermoplastic resin contg. rubber and specified carbon black. CONSTITUTION:100pts.wt. mixture of 5-95wt% arom. polycarbonate (A) having an average MW of 10,000 to 100,000, 5-95wt% thermoplastic polyester (B) having an intrinsic viscosity of 0.2 to 2.0 as measured in 0-chlorophenol at 25 deg.C (e.g., polyethylene terephthalate) and 0-20wt% thermoplastic resin (C) contg. rubber is blended with 1-10pts.wt. carbon black (D) having oil absorption of not smaller than 500ml/100g and a specific surface area of not smaller than 150m<2>/g as measured by the BET low-temperature nitrogen adsorption method. |