Resin composition for porous film and film prepared therefrom.

摘要

A porous film having a good water vapor permeability is obtained with a high productivity by melting a resin composition comprising 100 parts by weight of a polyolefin resin and 50 to 500 parts by weight of barium sulfate having an electric conductivity of 250 pS cm or less in terms of the electric conductivity of a supernatant formed when the barium sulfate is added to water, and a particle size of 0.1 to 7 µm, forming the melt into a film and stretching the film to 2.5 to 14 times the original area at least in the uniaxial direction.