| 摘要 |
The present invention provides a low density aluminum-base alloy, consisting essentially of the formula AlbalZraLibMgcTd, wherein T is at least one element selected from the group consisting of Cu, Si, Sc, Ti, V, Hf, Be, Cr, Mn, Fe, Co and Ni, "a" ranges from about 0.25-2 wt %, "b" ranges from 2.7-5 wt %, "c" ranges from about 0.5-8 wt %, "d" ranges from about 0.5-5% and the balance is aluminum. The alloy has a primary, cellular-dendritic, fine-grained, supersaturated aluminum alloy solid solution phase with intermetallic phases of the constituent elements uniformly dispersed therein. A consolidated article can be produced by compacting together particles composed of the aluminum alloy of the invention in a vacuum at elevated temperature. The compacted alloy is solutionized by heat treatment, quenched in a fluid bath, and optionally, stretched and aged. The microstructure of the consolidated article is composed of an aluminum solid solution containing a substantially uniform distribution of fine intermetallic precipitates.
|