摘要 |
Silver oxide for battery was produced by electrolyzing AgNO3 soln. with a current density of 200-250 mA/cm2. Thus, 150ml AgNO3 soln. was electrolysed for 4hr. with a current density of 200mA/ cm2 to give Ag7O8NO3, which was heated and dried to give 3g AgO powder.
|