FEUERFESTE, THIXOTROPE VIBRATIONS-MASSE SOWIE VERFAHREN UND VORRICHTUNG ZUR VIBRATIONSZUSTELLUNG VON METALLURGISCHEN GEFAESSEN MIT DIESER MASSE

摘要

1. A thixotropic self-curing refractory vibration mass based on zirconium silicate for achieving a vibration density of at least 3.6 g/cm**3 , characterized by the following chemical composition (in % by weight) : 24 to 29% SiO2 10 to 20% Al2 O3 0.2 to 0.8% P2 O5 0 to 1.5% K2 O+Na2 O+LiO2 0 to 0.5% Fe2 O3 0 to 0.05% CaO rest ZrO2 and the following crystallographic analysis (in % by weight) : 20 to 30% fused zirconium silicate/corundum 1 to 5% alumina 0.1 to 0.5% amorphous silica 0.3 to 1% aluminum metaphosphate 0.5 to 4% alkalisilicate with a molar ratio of -------------------1:2 to 1:4 rest zirconium silicate and having the following particle size spectrum : 26 to 32% 0 to 0.06 mm 32 to 52% 0.06 to 0.5 mm 23 to 38% as rest 0.5 to 3 mm.