CONTROL OF SEED MELT-BACK DURING DIRECTIONAL SOLIDIFICATION OF METALS

摘要

In the manufacture of a single crystal article, by the directional solidification of a metal in a ceramic mold the melt-back of a seed crystal is controlled to provide high casting yield. The melt-back, measured as a fraction of the original length of the seed, is preferably between 25-75%, more preferably between 33-67%. Diametrical clearance between the seed and mold is also closely controlled, between 0.06-0.25 mm, to eliminate extraneous grain nucleation.