| 摘要 |
PURPOSE:To obtain a wear resistant sintered hard alloy having superior oxidation resistance by combining a binding phase having a specified total content of Ni, Co, Mo, Cr and Ti, specified mutual ratios and a specified structure with the dispersed phase of a W-carbide having a specified grain size. CONSTITUTION:The binding phase consisting of NI, Co, Mo and Cr in Mo/(Ni+ Co+Cr+Mo)=1/50-1/10, Cr/(Ni+Co+Mo+Cr)=1/20-1/5 and Co/Mi=9/1-1/9 is combined with the dispersed phase of WC having 2-6mum average grain size. The total amount of Ni, Co, Mo and Cr is 10X30wt%, and the binding phase further contains 0.1-2wt% Ti and has a structure contg. a uniformly precipitated fine (Co,Ni)3Ti phase. The heat resistant WC-base sintered hard alloy having the high resistances to oxidation, heat, shock, hot wear and thermal fatigue is obtd.
|