摘要 |
PURPOSE:To produce an ammonium gallate composition having extremely high electrical conductivity, by adding ZnO to ammonium gallate at a specific molar ratio to 5Ga2O3, thereby forming a solid solution. CONSTITUTION:The objective ammonium gallate composition is produced by adding 0.01-1mol of ZnO (based on 1mol of 5Ga2O3) to ammonium gallate to form a solid solution. The ammonium gallate composition is a protonic conductive solid having extremely high electrical conductivity, e.g. of 4.4X10<28>/cm at 190 deg.C.
|