| 摘要 |
PURPOSE:To improve absorbing capacity and humidity conditioning capacity, by preparing a malodor absorbing material by forming a specific amount of a cellulose fiber, magnesium silicate clay mineral having an amorphous part and an org. binder into an integral solid substance. CONSTITUTION:100pts.wt. of a cellulose fiber, 50-3,000pts.wt. of magnesium silicate clay mineral having an amorphous part and 1,000-300,000pts.wt. of water are mixed to prepare a slurry. An org. binder is added to this slurry in an amount of 1-20pts.wt. to 100pts.wt. of the magnesium silicate clay mineral having the amorphous part on a solid basis. This slurry mixture is dehydrated and molded to form a semi-filter body which is, in turn, dried to obtain an integrally solidified malodor absorbing material. The size of the magnesium silicate clay mineral having the amorphous part is pref. 150mum or less. |