| 摘要 |
A novel process is provided for producing prefoam type cellular concrete articles, which uses a foamed slurry (E) consisting essentially of an aqueous slurry (A) of a calcium silicate-based cement compound, an aqueous slurry (B) of a calcium aluminate-based cement compound, a specific setting retarder (C), and an aqueous foamed liquid (D). The process is further characterized in that: (i) the foamed slurry (E) is cast and provided with hardened strength sufficient for demolding in 20 to 120 minutes after it has been poured into a mold; (ii) the demolded article is subjected to precuring under specific conditions of humidity, temperature and precuring time; and (iii) the molded article is then subjected to hydrothermal curing under high pressure. |