| 摘要 |
A continuous process is disclosed for the production of poly-(para-phenylene terephthalamide) and its copolymers, having an inherent viscosity of at least 3. Molten terephthaloyl chloride, and optionally adipoyl chloride, are reacted in stoichiometric amounts with a solution of para-phenylenediamine and/or of 4,4'-diaminoadipanilide, and optionally of a prepolymer formed from at least one chloride and at least one diamine from amongst those mentioned above, in a mixture of N-methylpyrrolidone-2 and calcium chloride which is homogeneous and substantially anhydrous, with a molar ratio of CaCl2/unit: <IMAGE> of at least 1, and preferably at least 1.15, and under conditions such that the final composition contains at least 5% by weight of polymer, relative to the N-methylpyrrolidone-2, where R represents p-phenylene or p-phenylene and up to 50% of n-butylene of the total polymer units. The polymer obtained may be converted into films, fibers and high-performance yarns for reinforcing composite materials or articles made of rubber. |