| 摘要 |
Grain refined palladium-based dental alloys contain about 70-85 weight percent palladium, 7-15 weight percent copper, 2-8 weight percent gallium, 2-15 weight percent indium, 0.2-3.0 weight percent rhenium or ruthenium and an effective amount of boron up to about 0.15% which eliminates the formation of bubbles in porcelain during the porcelain firing process. In addition, there can be an effective amount of zinc up to about 0.5 weight percent. Alternately, in lieu of zinc, the boron is added in the form of calcium boride.
|