The gelloid compositions comprise a crosslinked non-silicone polymer having an olefinic unsaturated content of less than 10 mole percent and having from 0.1 to 3 crosslinks per weight average molecule, having dispersed therein a liquid in an amount of from 20% to 95% by weight based on the weight of the dispersed liquid and polymer, and from 0 to 0.3 volume fraction of a filler, the composition having a storage modulus of (1 + 2.5v + 14.1v<2>)x dynes/cm<2> where x is less than 5x10<5> at 30 DEG C and greater than 5x10<3> at 90 DEG C, and v is the volume fraction of the filler, and having a dynamic viscosity of (1 + 2.5v + 14.1v<2>)y poises where y is less than 1x10<5> at 30 DEG C and greater than 3x10<3> at 90 DEG C and v is the volume fraction of the filler, and exhibiting first degree blocking. These compositions have good heat stability, low water and oil permeability, good adhesion and can usefully provide a layer of electrically insulating, stress grading or conducting material. |