<P>L'INVENTION CONCERNE UN ACIER INOXYDABLE FERRITIQUE ADDITIONNE DE P AYANT D'EXCELLENTES APTITUDES A LA MISE EN FORME ET OUVRABILITE SECONDAIRE.</P><P>SELON L'INVENTION, IL CONSISTE ESSENTIELLEMENT, EN EN POIDS: C: 0,0050 A 0,0500, CR: 10,00 A 18,00, SI: JUSQU'A 0,50, MN: JUSQU'A 0,50, P: PLUS DE 0,040 MAIS PAS PLUS DE 0,200, S: JUSQU'A 0,030, NI: JUSQU'A 0,60, SOL.AL: 0,005 A 0,200, ET B: TRACES JUSQU'A 0,0050, LE RESTE ETANT FE ET DES IMPURETES INEVITABLES, LES ELEMENTS D'ALLIAGE ETANT DE PLUS EQUILIBRES DE FACON QUE LE POINT AYANT LE POURCENTAGE REPRESENTE PAR LA FORMULE(CR 50P POUR L'ABSCISSE ET LE POURCENTAGE REPRESENTE PAR LA FORMULE (C 10B SOL. AL) POUR L'ORDONNEE PUISSE SE TROUVER DANS LA ZONE D'UN QUADRILATERE ABCD, OU LES POINTS A, B, C ET D ONT POUR COORDONNEES (12,0, 0,30), (12,0, 0,005), (22,0, 0,020) ET (22,0, 0,30), RESPECTIVEMENT.</P><P>L'INVENTION S'APPLIQUE NOTAMMENT A LA METALLURGIE.</P>
|