发明名称 |
Ceramic compositions comprising alumina |
摘要 |
A composition suitable for firing to obtain a ceramic material therefrom may include from about 1 to about 40 wt. % based on the total dry weight of the composition a first particulate material having a Mohs hardness of at least about 8.5 and a d50 of from about 7 μm to about 500 μm. The composition may include at least about 50 wt. % based on the total dry weight of the composition a second particulate material comprising alumina. The composition may include from 0 to about 10 wt. % based on the total dry weight of the composition a sintering aid. A green body or ceramic material may be formed from the composition. Ballistic armor may be formed from the composition or may include the ceramic material. |
申请公布号 |
US9416055(B2) |
申请公布日期 |
2016.08.16 |
申请号 |
US201314408274 |
申请日期 |
2013.06.21 |
申请人 |
Imerys Ceramics France |
发明人 |
Gasgnier Gilles;Zhang Wen |
分类号 |
C04B35/111;C04B35/117;F41H5/00;C04B35/101;C04B35/103;C04B35/106;C04B35/626;C04B35/645;F41H5/04;C04B35/64 |
主分类号 |
C04B35/111 |
代理机构 |
Finnegan, Henderson, Farabow, Garrett & Dunner LLP |
代理人 |
Finnegan, Henderson, Farabow, Garrett & Dunner LLP |
主权项 |
1. A composition suitable for firing to form a ceramic material therefrom, said composition comprising:
from about 1 to about 40 wt. % based on the total dry weight of the composition of a first particulate material having a Mohs hardness of at least about 8.5 and a d50 of from about 7 μm to about 500 μm, said first particulate material being fused corundum; at least about 50 wt. % based on the total dry weight of the composition of a second particulate material, said second material being calcined alumina other than fused corundum; and from 0 to about 10 wt. % based on the total dry weight of the composition of a sintering aid. |
地址 |
Paris FR |