| 摘要 |
PURPOSE:To provide an electrically conductive resin composition having extremely low increase in the resistance during kneading operation, and high mold releasability in injection molding, by compounding a thermoplastic synthetic resin with a metallic filler and a fatty acid salt of a metal having high ionization tendency. CONSTITUTION:A thermoplastic synthetic resin is compounded with a metallic filler and a fatty acid salt of a metal having high ionization tendency. The synthetic resin is preferably the one having a melt index of >=3. The metallic filler has a diameter of 10-600mu, preferably 30-100mu, and a length of 0.5- 200mm., preferably 2-6mm., and its amount is 7-15vol%. The fatty acid metal salt is the stearate, laurate, etc. of a metal having higher ionization tendency than aluminum, and its amount is 0.2-30wt%, preferably 0.5-5wt% based on the synthetic resin. |