| 摘要 |
<P>CES POLYETHERESTERAMIDES SEQUENCES THERMOPLASTIQUES SONT PREPARES PAR POLYCONDENSATION DE POLYAMIDES LINEAIRES PORTEURS DE GROUPES CARBOXYLE TERMINAUX AVEC DES QUANTITES PRESQUE EQUIMOLAIRES DE A, O-DIHYDROXYPOLYETHERS EN PRESENCE DE COMPOSES MINERAUX OU ORGANIQUES DE L'ETAIN (II) COMME CATALYSEURS D'ESTERIFICATION. LES POLYAMIDES ONT COMME PRODUITS DE DEPART LES MONOMERES DE PA-6, -11, -12, -6.6, -6.9, -6.12, -6.13 OU DES MELANGES DE CES MONOMERES AVEC UN DIACIDE CARBOXYLIQUE ALIPHATIQUE, LINEAIRE OU RAMIFIE, OU UN DIACIDE CARBOXYLIQUE AROMATIQUE OU CYCLOALIPHATIQUE. LE POIDS MOLECULAIRE DES POLYAMIDES MIS EN OEUVRE EST DE 700-15000, CELUI DES DIHYDROXY-POLYETHERS DE 400-4000. LA POLYCONDENSATION SE DEROULE SOUS LA PRESSION NORMALE OU REDUITE, ET A DES TEMPERATURES DE 210-280C.</P><P>APPLICATION DE CES POLYETHERESTERAMIDES SEQUENCES THERMOPLASTIQUES A LA FABRICATION DE PIECES INJECTEES OU MOULEES PAR ROTATION, D'ARTICLES EXTRUDES, DE FIBRES ET DE FEUILLES.</P>
|