A rotted wood stabilizer composition is provided, the composition comprisin g: from about 75 to about 90 weight percent of a crosslinking polymer; from abo ut 1.5 to about 0.5 to about 1.5 weight percent of a film forming agent, and from about 8 to about 15 weight percent water, and optionally further comprising a biocide a nd a defoamer. The composition preferably has a pH in the range of from about 2.8 to about 3.0. Further the composition preferably has a viscosity of between abo ut 750 to about 1250 cps as measured on a BROOKFIELD RV viscometer (helipath on) with a #2 T/E spindle at about 12 rpm and about 25.degree.C. The invention further provides for methods of manufacturing the composition, as well as for method s of repairing a rotted area of a wood component by applying the composition of t he present invention.
|