| 摘要 |
PURPOSE:To provide the titled resin compsn. having excellent flow characteristics, low-temperature impact resistance, etc., by blending a hindered phenol compd. and/or an arom. amine with a mixture of a polyamide and a modified polyolefin having functional groups. CONSTITUTION:95-50wt% polyamide is mixed with 5-50wt% modified polyolefin having functional groups selected from carboxyl, carboxylate metal salt, carboxylate ester, anhydride, and epoxy groups, such as an ethylene/acrylic acid copolymer. 0.02-3pts.wt. hindered phenol compd. such as 3,5-di-t-butyl-4- hydroxytoluene and/or arom. amine such as N,N'-di-beta-naphthyl-p-phenylenediamine are/is blended with 100pts.wt. above mixture to obtain the desired polyamide resin compsn. |