Coating compositions for solar selective absorption comprising a thermosetting acrylic resin and particles of a low molecular weight fluorocarbon polymer

摘要

A coating composition for solar selective absorption comprising, in solvent, particles of an inorganic black pigment dispersed in a dissolved binder of a thermosetting acrylic resin and particles of a low molecular weight fluorocarbon resin contained in an amount of 5-15 parts by weight per 100 parts by weight of the acrylic resin. The inorganic black particles have a size of 0.01-0.5 microns and are contained in an amount of 45-65 parts by weight per 100 parts by weight of the acrylic resin. An article having a metal substrate and a paint film formed thereon from the composition in a dry thickness of 1.5 microns or more is also described.