Process for preparing alkali metal salt of carboxymethyl cellulose

摘要

A process for preparing a form of carboxymethyl cellulose which exhibits superior rheological and fluid loss characteristics in aqueous calcium chloride solutions which comprises conducting causticization of high molecular weight cellulose in the absence of oxygen, at a temperature less than 350 DEG C., in an aqueous solution containing 86.9+/-2% by weight isopropanol, at an isopropanol-water solution to cellulose weight ratio from 2 to 1 to 7.5 to 1, and in the presence of sufficient alkali metal hydroxide such that the alkali metal hydroxide to monochloroacetic acid molar ratio during the subsequent etherification of the alkali cellulose is greater than 2.00 to 1, wherein the monochloroacetic acid utilized contains less than about 2% by weight dichloroacetic acid.