Acoustic vibrating element of graphite and method of manufacturing same

摘要

An acoustic vibrating element, such a domed speaker diaphragm A or a phonographic pickup cantilever B, is formed by vapor deposition on an easily separable mold member 5 of tantalum or tantalum alloy when a mixture of a hydrocarbon gas and an inert gas is passed through a furnace heated to a temperature of 1150 DEG C.-1250 DEG C. at a flow rate in excess of 200 cm/min. The c-axis crystalline orientation of the resulting graphite element is substantially perpendicular to its surface, which provides a Young's modulus above 16,000 Kg/cm2.