New compositions consisting of 40-75 percent by weight of amorphous 1,2-polybutadiene having a molecular weight above 50,000 and 25-60 % by weight of 1,4-cis polybutadiene having a molecular weight above 100,000 result in sulfur vulcanizates having a low brittle point, a high elasticity modulus, and a low rebound and which swell to a relatively low degree when immersed in benzene.
|