| 摘要 |
PURPOSE:The titled composition which gives a molded part having a beautiful surface, and excellent plate adhesion and impact resistance, and is obtained by incorporating an oxide of a Group II metal of the periodic table, sulfur or a sulfurliberating compound, a vulcanization accelerator, and a specified carbon black into an olefin resin. CONSTITUTION:100pts.wt. olefin resin (A) (e.g. polyethylene), 0.1-10pts.wt. oxide of a Group II metal of the periodic table (B) (e.g. zinc oxide), 0.1-10pts.wt. sulfur or a sulfurliberating compound (C), 0.05-10pts.wt. vulcanization accelerator (D) (e.g. thiazole type) and 5-60pts.wt. carbon black (E) having a resistivity under a pressure of 50kg/cm<2> of 0.30OMEGA.cm or less, a hydrochloric acid absorption of 20-40ml/5g, and a specific surface of 100-400m<2>/g are compounded to give an olefin resin composition for electroplating which gives a molded part having a beautiful surface and improved impact resistance while maintaining desirable physical properties. |