| 摘要 |
PURPOSE:To provide the titled compsn. having excellent flow characteristics during molding and capable of forming a molded article which little suffers deterioration of strength and dimensional changes due to water absorption, by blending a polyamide resin, a polypropylene resin and a reinforcing fiber in a specified ratio. CONSTITUTION:60-120wt% (based on the combined amount of components A and B mentioned below) reinforcing fiber such as glass fiber is melt-mixed with a mixture consisting of 75-95pts.wt. polyamide resin (A) having a m.p. of 200 deg.C or higher and a relative viscosity (JIS-K6810-1970) of 1.8 or above, such as nylon 6 or nylon 12, and 25-5pts.wt. polypropylene resin (B) having a flow index (230 deg.C, 2.16kg) of 30g/10min such as a resin obtd. by grafting maleic anhydride onto isotactic polypropylene. |