摘要 |
A process comprising the steps of adding an inorganic foamed aggregate, an inorganic solid aggregate and a reinforcing fiber to cement to prepare a cement mixture, kneading the cement mixture with addition of 3 to 15% by weight of water based on the mixture to obtain a relatively hard kneaded mixture, press-molding the kneaded mixture at pressure of 200 to 600 kg/cm2, adding water to the molded piece to adjust the water content thereof, preheating the molded piece at a temperature of 40 DEG to 70 DEG C. before curing, spraying to the surface of the heated molded piece an aqueous dispersion prepared from resin and cement-type coloring material and containing inorganic particles 0.1 to 1.5 mm in size, drying the coated piece, applying a colored resin composition to the coating, and curing the resulting piece in an autoclave with pressurized steam, whereby a colored roofing panel or like cement product can be prepared. |