Nitrile rubber composition having high modulus

摘要

A method of preparing a nitrile rubber composition having modulus and excellent physical properties and abrasion resistance is disclosed. This composition is prepared by kneading at 120 DEG -160 DEG C. (a) a nitrile rubber, (b) an alpha , beta -ethylenically unsaturated carboxylic acid, (c) a divalent metal compound, (d) a secondary aryl amine, cooling the kneaded mass below 100 DEG C., adding to the kneaded mass (e) an organic peroxide, and heating and curing the resulting mixture at 110 DEG -180 DEG C. The addition of the secondary aryl amine considerably improves the physical properties of the composition. These compositions have not a tendency of scorching and are superior in the workability as compared with conventional carboxylated nitrile rubber compositions produced by emulsion polymerization.