<P>L'INVENTION EST RELATIVE A UNE METHODE INTERROMPUE DES ALLIAGES D'ALUMINIUM A DURCISSEMENT STRUCTURAL.</P><P>ELLE COMPREND, A PARTIR DE LA MISE EN SOLUTION:</P><P>A.UN REFROIDISSEMENT RAPIDE, PAR TREMPE JUSQU'A CE QUE LE PRODUIT ATTEIGNE UNE TEMPERATURE COMPRISE ENTRE 150 ET 260C.</P><P>B.UN ARRET DE LA TREMPE PENDANT QUELQUES SECONDES A QUELQUES DIZAINES DE MINUTES (REFROIDISSEMENT A L'AIR)</P><P>C.UNE REPRISE DE LA TREMPE JUSQU'A LA TEMPERATURE AMBIANTE.</P><P>DANS CES CONDITIONS, ON OBTIENT DES PRODUITS TREMPES REVENUS QUI PRESENTENT DES CARACTERISTIQUES MECANIQUES VOISINES DE L'ETAT T6 ET SUPERIEURES A CELLES DE L'ETAT T73 CLASSIQUE, AVEC UNE TRES BONNE RESISTANCE A LA CORROSION (FEUILLETANTE OU SOUS TENSION) ET UN NIVEAU DE CONTRAINTES INTERNES DIVISE SENSIBLEMENT PAR 2 PAR RAPPORT A L'ETAT T6 CLASSIQUE.</P><P>CE TRAITEMENT EST APPLICABLE A TOUS LES ALLIAGES D'AL DES SERIES 2000, 6000 ET 7000.</P>
|