| 摘要 |
<p><P>L'INVENTION A POUR OBJET UNE FIBRE DE CARBONE DE HAUTES PERFORMANCES, UN PROCEDE POUR SA PRODUCTION, ET DES MATERIAUX COMPOSITES PREPARES A PARTIR DE CELLE-CI.</P><P>CETTE FIBRE A UN DIAMETRE DE FILAMENT UNIQUE DE 2 A 6MICRONS ET PRESENTE UNE RESISTANCE DE NOEUD DU FIL D'AU MOINS 7KG LORSQU'ELLE EST MISE SOUS FORME D'UN FIL DE 0,4 0,01G PAR METRE.</P><P>ELLE EST PREPAREE PAR UN PROCEDE CONSISTANT A SOUMETTRE UNE FIBRE A BASE D'ACRYLONITRILE DE 0,1 A 0,6DENIER AYANT UNE RESISTANCE A LA TRACTION D'AU MOINS 6G PAR DENIER A UN TRAITEMENT DE PREOXYDATION CONSTITUE: A.PAR UN PREMIER TRAITEMENT DE PREOXYDATION DANS LEQUEL ON TRAITE LA FIBRE D'ACRYLONITRILE SOUS UNE TENSION TELLE QUE L'ON OBTIENNE UN RETRAIT D'AU MOINS 3 JUSQU'A CE QUE LA TENEUR EN EAU A L'EQUILIBRE ATTEIGNE 5, ET B.PAR UN SECOND TRAITEMENT DE PREOXYDATION DANS LEQUEL ON TRAITE LA FIBRE A BASE D'ACRYLONITRILE SOUS UNE TENSION TELLE QUE L'ON AIT UN RETRAIT D'AU MOINS 1, CE TRAITEMENT DE PREOXYDATION ETANT EFFECTUE EN ATMOSPHERE OXYDANTE A UNE TEMPERATURE DE 240 A 300C, LA RELATION ENTRE LE TEMPS DE PREOXYDATION T (MINUTES) ET LA TEMPERATURE DE TRAITEMENT DE PREOXYDATION MOYENNE T (C) SATISFAISANT L'EQUATION(I):(310 - T) (0,8 3) T(I)ET A SOUMETTRE LA FIBRE AINSI PREOXYDEE A UN TRAITEMENT DE CARBONISATION DANS UN GAZ INERTE MAINTENU A 1000C-1800C.</P></p> |