| 摘要 |
<p>PURPOSE:To provide the titled compsn. which can produce molded articles having good flexural properties and heat resistance and excellent chemical resistance, moisture absorption resistance and surface properties, by blending a polyolefin resin, a polyamide resin, an ionomer and a reinforcing filler together. CONSTITUTION:A polyolefin resin (A) (e.g. polypropylene resin), a polyamide resin (B) (pref. a resin having a m.p. of 200 deg.C or higher; e.g. nylon 6), an ionomer (C) [a copolymer of an olefin with an ethylenically unsaturated monomer contg. a metal carboxylate group; pref. a copolymer having a melt index of 0.2-1,000g/ 10min.], and a fibrous reinforcing agent and/or an inorg. filler (D), are blended together. The blending ratio of component A to component B is 40-60:95-5 (by weight). Component C is used in an amount of 0.5-20wt% based on the combined amount of components A and B. The fibrous reinforcing agent is used in an amount of 5-10wt%, and the inorg. filler is used in an amount of 0.1-10wt% based on the combined amount of components A and B.</p> |