摘要 |
A process for the production of a porous ceramic mold is described, compsiging adding about 40 to 60 parts by weight of water to 100 parts by weight of a ceramic material, mixing the thus-formed ceramic slurry with about 20 to 40 parts by weight of a hydrophilic urethane prepolymer having a free isocyanate group content of from about 4% to 7% by weight, reacting and foaming the resulting mixture after the introduction thereof into a mold, drying the thus-formed foamed urethane molded article, and combusting very slowly and sintering the dried foamed urethane molded article to produce a porous ceramic molded article. |