| 摘要 |
A thermally stable, pure transition alumina extrudate suitable for use as a catalyst support has a uniquely defined bimodal pore size distribution and very good mechanical properties. Most of the surface area is in a micropore region having pores of less than 500 Angstrom units, a pore volume of 0.60 to 0.80 cm.3/g., a narrowly defined effective pore volume distribution within this region and a median pore diameter which can be controlled within the range of 90-210 Angstrom units. The macropore region made of pores having diameters of 1,000- 10,000 Angstrom units has a pore volume of at least 0.10 cm.3/g. These two pore volumes are essentially connected directly to each other. The extrudates can be strengthened by acidic additives and given increased thermal stability by adding rare earth oxides. |