| 摘要 |
<P>LA PRESENTE INVENTION CONCERNE DES ALLIAGES DE TITANE-ALUMINIUM-NIOBIUM DU TYPE TIAL.</P><P>DANS CES ALLIAGES ON REGLE AVEC PRECISION LA TENEUR EN ALUMINIUM PARCE QU'UN EXCES D'ALUMINIUM DIMINUE LA DUCTILITE A TEMPERATURE AMBIANTE ALORS QU'UNE QUANTITE INSUFFISANTE DIMINUE LA RESISTANCE AU FLUAGE. LES ALLIAGES SELON L'INVENTION COMPRENNENT, EXPRIMES EN POURCENTS ATOMIQUES, 24-27 AL, 11-16 NB ET LE COMPLEMENT EST DU TI. ON PEUT REMPLACER LE NIOBIUM PAR DU VANADIUM EN QUANTITE S'ELEVANT JUSQU'A 4 ATOMIQUES REDUISANT AINSI LA DENSITE ET AUGMENTANT LE RAPPORT RESISTANCE A DENSITE TOUT EN MAINTENANT LES PROPRIETES.</P><P>L'INVENTION EST PAR EXEMPLE UTILISABLE DANS L'INDUSTRIE DES MOTEURS A TURBINE A GAZ.</P>
|